艾力特AT鞣剂在浸酸与不浸酸工艺体系下的鞣制性能

王思懿1, 强西怀1,*, 李闻欣1, 段郑军2, 张江山2, 郑超斌2   

  1. 1.陕西科技大学轻工科学与工程学院 轻化工程国家级实验教学示范中心,陕西 西安 710021;
    2.北京泛博清洁技术研究院有限公司,北京 102600
  • 收稿日期:2023-12-06 修回日期:2024-01-08 接受日期:2024-01-10 出版日期:2024-06-01 上线日期:2024-04-25
  • 通讯作者: *强西怀(1963-),男,工学博士,教授,主要研究方向:制革与毛皮清洁生产技术及其绿色化学品应用。E-mail:qiangxihuai@163.com。
  • 作者简介:王思懿(1999-),女,硕士研究生,主要研究方向:清洁化制革生产。E-mail:wsy18054422@163.com。
  • 基金资助:
    陕西科技大学研究生创新基金

Tanning Performance of the EIT AT Tanning Agent in Pickling and Non-pickling Tanning Systems

WANG Siyi1, QIANG Xihuai1,*, LI Wenxin1, DUAN Zhengjun2, ZHANG Jiangshan2, ZHENG Chaobin2   

  1. 1. College of Bioresources Chemical and Materials Engineering, Shaanxi University of Science&Technology, Xi’an 710021, China;;
    2. Beijing Fanbo Clean Technology Research Institute, Beijing 102600, China
  • Received:2023-12-06 Revised:2024-01-08 Accepted:2024-01-10 Published:2024-06-01 Online:2024-04-25

摘要: 以绵羊酸皮为实验对象,使用新型有机鞣剂艾力特AT分别在常规浸酸和不浸酸两种工艺体系下进行鞣制,通过坯革的收缩温度、纤维形貌及其热力学性能等分析测试,主要考察艾力特AT鞣剂在浸酸与不浸酸工艺体系下鞣制性能的差异性。实验结果表明:在两种工艺体系中,鞣制工艺条件的变化对鞣制效果产生了相似的影响;在艾力特AT鞣剂用量6%时,两种不同工艺体系下鞣制的坯革收缩温度都可以达到89 ℃。此外,鞣制坯革粒面饱满,毛孔清晰,热稳定性和力学性能基本接近。因此,艾力特AT鞣剂在浸酸与不浸酸工艺条件下,基本鞣制效应差异性不明显,这对于推广和应用基于艾力特AT鞣剂的无铬鞣制技术具有一定的理论指导意义。

关键词: 艾力特AT, 无铬鞣剂, 无铬鞣制, 制革

Abstract: This study aimed to investigate the tanning performance of a newly organic chromium-free tanning agent, EIT AT. The pickled sheepskins were used in the experiment. By using two different tanning systems: conventional pickling and non-pickling, the shrinkage temperature, fiber morphology, and thermodynamic properties of tanned leather were analyzed. The results showed that the change of variations in tanning process has a similar impact on the tanning effect in two different tanning systems. At the 6% amount of EIT AT, the shrinkage temperature of the crust leather can reach above 89 ℃; The crust leather exhibited full grain and clear pores, as well as similar thermal stability and mechanical properties in two different tanning systems. Therefore, the tanning effect of EIT AT tanning agent shows less differences with pickling or non-pickling conditions. The results provide a certain theoretical guidance for the popularization and application of chromium-free tanning technology with EIT AT tanning agent.

Key words: EIT AT, chromium-free tanning agent, chrome-free tanning, leather manufacture