水热辅助酸法的革屑脱铬研究

doi:10.19677/j.issn.1004-7964.2022.02.005

皮革科学与工程 ›› 2022, Vol. 32 ›› Issue (2): 26-31.doi: 10.19677/j.issn.1004-7964.2022.02.005

水热辅助酸法的革屑脱铬研究

王邵腾, 陈慧^*, 单志华^*

四川大学制革清洁技术国家工程室,四川成都 610065

收稿日期:2021-10-15 出版日期:2022-04-28 上线日期:2022-03-22
通讯作者: *
作者简介:王邵腾（1995-）,男,2019级硕士研究生,E-mail：1099566001@qq.com。
基金资助:
企业委托项目（基于污泥低铬及可循环利用的制革工艺及关键材料研究19H0921）

Study on Chromium Removal of Leather Scraps by Hydrothermal Assisted Acid Method

WANG Shaoteng, CHEN Hui^*, SHAN Zhihua^*

National Engineering Laboratory for Clean Technology of Leather Manufacture, Sichuan University, Chengdu 610065, China

Received:2021-10-15 Online:2022-04-28 Published:2022-03-22

摘要/Abstract

摘要： 采用草酸钠脱铬率达到94.9%后革屑表面形貌和热稳定性发生了显著变化。进一步用水热法处理脱铬革屑制得革屑水解物。结果表明在脱铬革屑固含量为10%,温度为110 ℃条件下,于水热釜中反应7 h,得到重均相对分子质量M_w=2.86 ×10⁵,灰分含量为0.530 %,铬含量为944 mg/kg的革屑水解物。可见采用草酸钠浸出铬和水热法联用的方式可以得到相对分子质量较高、灰分较低的革屑水解物,为铬革屑资源化提供新途径。

关键词: 制革工业, 铬革屑, 革屑水解物, 资源化利用

Abstract: The surface morphology and thermal stability of leather scraps were significantly changed by using sodium oxalate to remove chromium 94.9%.The hydrolysate of collagen was further prepared by hydrothermal treatment of dechromed leather scraps.The results showed that the collagen hydrolysate with a heavy average molecular weight M_w=2.86×10⁵ g/mol, an ash content of 0.530% and a chromium content of 944 mg/kg was obtained by reacting the dechromated leather scraps at a solid content of 10% and a temperature of 110 ℃ for 7 h in a hydrothermal reactor.It can be seen that the combination of chromium leaching by sodium oxalate and hydrothermal method can obtain collagen hydrolysate with high molecular weight and low ash content,which can provide a novel way to resource the chromium leather scraps.

Key words: tanning industry, chrome leather scraps, collagen hydrolysate, resource utilization

中图分类号:

TS59

王邵腾, 陈慧, 单志华. 水热辅助酸法的革屑脱铬研究[J]. 皮革科学与工程, 2022, 32(2): 26-31.

WANG Shaoteng, CHEN Hui, SHAN Zhihua. Study on Chromium Removal of Leather Scraps by Hydrothermal Assisted Acid Method[J]. Leather Science and Engineering, 2022, 32(2): 26-31.

参考文献

[1] 赵胜宗,刘彦.铬革屑的酸碱联合处理中CaO脱铬的优化[J].皮革科学与工程,2020,30(01):17-22.
[2] Fang C,Jiang X,Lv G,et al.Nitrogen-containing gaseous products of chrome-tanned leather shavings during pyrolysis and combustion[J].Waste Management,2018,78:553-558.
[3] 张文斌,王全杰,韩静,等.含铬革屑的再生资源化进展[J].皮革科学与工程,2016,26(02):39-42.
[4] Popiolski A S,Dallago R M,Steffens J,et al.Ultrasound-assisted extraction of Cr from residual tannery leather:feasibility of ethylenediaminetetraacetic acid as the extraction solution[J].ACS omega,2018,3(11):16074-16080.
[5] J.H.Muyonga,C.G.B.Cole,K.G.Duodu.Extraction and physico-chemical characterisation of Nile perch(Lates niloticus)skin and bone gelatin[J].Food Hydrocolloids,2004,18(4):581-592.
[6] 李宜航,唐文力.热水法提取鱼鳞明胶的最佳条件研究[J].广州化工,2021,49(11):67-69.
[7] 余艳. 高压处理法萃取鱼皮明胶[J].明胶科学与技术,2006,(03):148-152.
[8] Wang L,Chen M,Li J,et al.A novel substitution-based method for effective leaching of chromium(III)from chromium-tanned leather waste:The thermodynamics,kinetics and mechanism studies[J].Waste Management,2020,103:276-284.
[9] Oliveira L C A,Goncalves M,Oliveira D Q L,et al.Solid waste from leather industry as adsorbent of organic dyes in aqueous-medium[J].Journal of hazardous materials,2007,141(1):344-347.
[10] Nogueira F,Prado N,Oliveira L,et al.Incorporation of mineral phosphorus and potassium on leather waste(collagen):A new NcollagenPK-fertilizer with slow liberation[J].Journal of Hazardous Materials,2010,176(1-3):374-380.
[11] Wei,Q.Y.,1979.Tanning Chemistry of Leather.Light Industry Press,China,pp.88-97.
[12] Peng T,Zhu J,Huang T,et al.Facile preparation for gelatin/hydroxyethyl cellulose‐SiO₂ composite aerogel with good mechanical strength,heat insulation,and water resistance[J].Journal of Applied Polymer Science,2021,138(23):50539.
[13] 张一炜,杨健根,李圣强,等.制革含铬革屑减量及铬稳定化探索[J].皮革科学与工程,2017,27(03):17-21.
[14] Yi J,He T,Jiang Z,et al.AlCl₃ catalyzed conversion of hemicellulose in corn stover[J].Chinese Journal of Catalysis,2013,34(11):2146-2152.
[15] da Trindade Alfaro A,Fonseca G G,Balbinot E,et al.Yield,viscosity,and gel strength of wami tilapia(Oreochromis urolepis hornorum)skin gelatin:Optimization of the extraction process[J].Food Science and Biotechnology,2014,23(3):765-773.
[16] 郑翔,高沛汝,秦梦,等.制革固体废弃物的热-酶结合法制备明胶的研究[J].河北省科学院学报,2021,38(03):48-55.
[17] 张兵,王毅虎,王颖,等.酸法明胶、碱法明胶及酶法明胶的分子量分布分析[J].明胶科学与技术,2012,32(04):180-189.
[18] 丁晓良,王邵腾,蒲红霞,等.含铬革屑胶原降解物对硅酸盐水泥的缓凝影响[J].中国皮革,2021,50(07):85-90.
[19] Tian Z,Wang Y,Wang H,et al.Regeneration of native collagen from hazardous waste:chrome-tanned leather shavings by acid method[J].Environmental Science and Pollution Research,2020,27(25):31300-31310.

水热辅助酸法的革屑脱铬研究

Study on Chromium Removal of Leather Scraps by Hydrothermal Assisted Acid Method

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	彭良琼, 林诗雨, 郭丽君, 张文华, 石碧, 廖学品. 含铬革屑负载亚铁氰化铜钾对铯的快速吸附[J]. 皮革科学与工程, 2023, 33(5): 8-15.
[2]	唐余玲, 郭丽君, 周建飞, 石碧. 含铬革屑生物炭活化过硫酸盐降解亚甲基蓝[J]. 皮革科学与工程, 2023, 33(4): 1-6.
[3]	丁绍兰, 刘云, 李重遥. 耐铬厌氧胶原蛋白水解菌的筛选及应用研究[J]. 皮革科学与工程, 2022, 32(3): 30-35.
[4]	王文靖, 卢欣雨, 张晓伟, 刘彦. 碱酶一步法水解铬革屑的工艺研究[J]. 皮革科学与工程, 2021, 31(4): 40-45.
[5]	郭瑞军, 董亚琪, 杨茂, 鹿文慧, 李彦春. 四种胶原蛋白基皮革填充材料的应用研究[J]. 皮革科学与工程, 2020, 30(2): 48-52.
[6]	赵胜宗, 刘彦. 铬革屑的酸碱联合处理中CaO脱铬的优化[J]. 皮革科学与工程, 2020, 30(1): 17-22.
[7]	张东方;刘晓文;刘彦;. 碱-酶两步法水解铬革屑工艺条件优化[J]. , 2018, 28(05): 36-41.
[8]	. 《皮革科学与工程》2017年全年总目次[J]. , 2017, 27(06): 77-79.
[9]	陈沛海;王全杰;罗艳华;段宝荣;. 铬革屑制备功能有机肥改善荞麦品质的研究[J]. , 2017, 27(04): 19-.
[10]	罗艳华;陈沛海;李静;王全杰;石磊;. 含铬革屑碱水解的前期平衡研究[J]. , 2017, 27(01): 25-29.
[11]	单志华;陈慧;. 制革工业亟待迈出低谷[J]. , 2016, 26(06): 23-28.
[12]	栾俊;刁屾;陈沛海;王全杰;. 革屑资源化利用研究进展[J]. , 2016, 26(05): 28-34.
[13]	尹岳涛;段徐宾;石传晋;李幸;. 蒙脱土的改性及其在制革工业中的应用进展[J]. , 2016, 26(02): 28-34.
[14]	张文斌;王全杰;韩静;魏星星;曲敬轩;. 含铬革屑的再生资源化进展[J]. , 2016, 26(02): 39-42.
[15]	栾俊;王全杰;王闪闪;刁屾;张文斌;曲敬轩;. 微生物处理制革废弃物研究进展[J]. , 2015, 25(06): 28-33.